Alumina Carbon Brick

Short Description:

Alumina Carbon Brick IntroductionAlumina carbon brick is also called aluminum carbon firebrick. It is a carbon based refractory material made from corundum (high grade bauxite, mullite, etc.) aggregat...


  • · strong corrosion resistance,
  • · good thermal shock stability,
  • · high strength,
  • · high thermal conductivity.
  • ·
  • ·

Product Detail

Alumina Carbon Brick Introduction

 

Alumina carbon brick is also called aluminum carbon firebrick. It is a carbon based refractory material made from corundum (high grade bauxite, mullite, etc.) aggregates and fines, graphite, binders and additives. According to

 the production process, alumina carbon composite refractory bricks are divided into burned aluminum carbon bricks and unburned aluminum carbon bricks.

 

Catalogue

 

What are the Common Alumina Carbon Brick


    Burned Micropores Alumina-Carbon Brick

    Burned Micropores Alumina-Carbon Brick features

    Burned Microporous Alumina-Carbon Brick Technique Data

    Aluminium Carbon based Refractories for Continuous Casting Tundish


Aluminum Carbon Bricks Application

Aluminum Carbon Bricks Manufacture Process

What are the Raw Materials and Binders of Aluminum Carbon Bricks

 


What are the Common Alumina Carbon Brick

 

1.Burned Micro-pores Alumina-Carbon Brick is mainly used for working lining of bosh above the air pip and belly. The average pore diameter of micro-pore alumina carbon brick is less than 1µm, and the volume percentage of 

the pores less than 1µm is no less than 70%.

 

Burned Microporous Alumina-Carbon Brick features

 

(1) Low porosity & low air permeability.

(2) high crushing strength & high thermal conductivity.

(3) Anti-slag, anti-alkali, anti-erosion ability.

(4) Good thermal shock stability.

 

Burned Microporous Alumina-Carbon Brick Technique Data

ItemIndex
AC-1AC-2AC-3
Al 2 O 3 ,% ≥656055
C,% ≥11119
Fe 2 O 3 ,% ≤1.51.51.5
Bulk density, g/cm 3 ≥2.852.652.55
Apparent porosity, % ≤161718
Cold crushing strength, Mpa ≥706050
Refractoriness under load(0.2Mpa, Ti) °C ≥165016501600
Thermal shock stability, times ≥100100100
Iron liquid corrosion index,% ≤234
Air permeability, mDa ≤0.522
Average pore size, mm≤0.511
Less than 1mm Pores volume percentage % ≥807070
Anti-alkali performance,% ≤101015
Thermal conductivity, w/m·k ≥131313

 

2. Aluminium Carbon Refractories ued for Continuous Casting Tundish, mainly include upper nozzle, lower nozzle and stoppers, which are also called special-shaped aluminum carbon bricks. The raw materials of ontinuous

 casting nozzles and stoppers are corundum and graphite. A small amount of additives are added into raw materials during production process. Phenolic resin is used as binder of alumina carbon nozzles and stoppers. 

After mixing, molding and drying, green bodies are burned in non-oxidizing firing kiln. The firing temperature is 1350 °C, after machining, anti-oxidation coating can be spayed to the surface to prolong their service life.

 

Aluminium Carbon Refractories for Continuous Casting Tundish

 

(1) Good integrity and safe use.

(2) To better purify the molten steel.

(3) High strength, good resistance to molten steel and slag erosion.

(4) Wear resistance and long service life.

 

 Aluminum Carbon Bricks Application

 

Aluminum carbon bricks can be used in blast furnaces, continuous casting tundishes (long nozzles, submerged nozzles, stoppers, upper and lower nozzle bricks, slide plate bricks), ladle, hot metal cans, torpedoes and other

 thermal equipment.

 

Aluminum Carbon Bricks Manufacture Process

 

Add graphite raw materials to alumina raw materials (corundum, mullite, bauxite), add small amounts of other raw materials such as silicon powder and SiC powder, then mixed with resin or asphalt binder, molded by press 

machine and finally fired at about 1300 ° C in a reducing atmosphere kiln.

 

What are the Raw Materials and Binders for Making Aluminum Carbon Bricks

 

For the unfired aluminum carbon bricks, the commonly used raw materials are: corundum, mullite, first-grade high-alumina bauxite clinker, graphite, SiC and Si powder. Commonly used binding agents are: resin, tar, asphalt 

and the like. Different raw materials should be used for the production of aluminum carbon bricks based on applications.


The above is a brief introduction of aluminum carbon bricks. If you need to purchase aluminum carbon bricks, can supply you the best quality products with competitive price. We can also customize refractory 

products according to your requirements and provide you best refractory materials and engineering solutions.